n of lead and zinc ores.
ZnSO4 (Zinc Sulfate)
- mol wt : 161.44
- O : 39.64%, S : 19.86%, Zn : 40.50%
- Monohydrate, dried zinc sulfate.
- Powder or granules
- Sol in water, practically isol in alcohol
- Odorles crystals or granules or powder
- Efflorescent in dry air
- d : 1.97, m.p : 100°
- One gram dissolves in 0.6ml water
- Use : As mordant in calico-printing ; preserring wood and skins ; with hypo-chlorite for bleaching paper. manuf lithpone and other zinc salts ; clarifying glue ; electrodepositing Zn ; also as reagent in analytical chemistry.
Lime (Calcium Oxide)
- mol wt : 56.08
- Ca : 71.47%, O : 28.53%
- Properly stored lime of commerce contains 90~95% free CaO.
- Commercial production from limestone.
- Crystals, white or grayish-white humps, or granular powder.
- m.p : 2572°, b.p : 2850°, d 3.32~3.35
- Sol in water forming Ca(OH)2 and generating a large quenting of heat.
H2SO4 (Sulfuric Acid)
- mol wt : 98.08
- H : 2.06%, O : 65.25%, S : 32.69%
- Sulfuric acid of commerce contains 93~98°
- Clear, colorless, odorless, oily liquid.
- d : 1.84, b.p : 290°
Na2CO3 (Sodium Carbonate)
- mol wt : 106.00
- C : 11.33%, Na : 43.39%, O : 45.29%
- Occurs in nature as the hydrate, thermonatrite, and the decahydrate, natron or natrite.
- Odorless, hygroscopic powder.
- m.p : 851°, d : 2.53
- Use : In manuf of Na salts, glass, soap ; for washing wood ; textiles, etc ; in bleaching linen, cotton ; general cleanser ; in water - softening in photography
(3). 실험 장치
실험에서 사용된 부유화 장치는 회분식으로 작동하는 배부유화통(WEDAG)인 실험실적 부유화 용기로 그림 6에 개략적으로 나타내었다. 기계적 교반과 현탁액내의 공기공급은 위쪽 축S와 연결된 임펠러 I의 회전으로 이루어진다. 회전체는 공기 입구 A를 지나 임펠러축내 공간을 통해 들어오는 공기와 H관을 통해 들어오는 현탁액을 밑으로 끌어내린다. 완전한 교반후 기포가 섞인 현탁액은 임펠러 주위의 정체 공간으로 배출된다. 임펠러의 속도는 계속적으로 조절되며 공기의 유입은 밸브V에 의해서 조절된다. 표시 M까지 채운 용기의 부피는 2.5ℓ이다. 부유화된 광물은 손긁개에 의해서 지점 O로 흘러내리게 한다.
그림 6. 개략적으로 그린 실험실용 부유화 장치
(4). 실험 방법
본격적인 실험 절차는 다음과 같다.
1. 광석을 cross beater mill로 거의 혹은 완전히 광물이 유리될 때까지 분쇄한다.
2. 채로 쳐서 0.06~0.15mm사이의 광물 입자를 준비한다.
3. 물과 150g의 광석 분말을 혼합한 현탁액을 부유화 용기 내에 표시
된 지점(약 2.5ℓ)까 지 가득 채운다.
4. PbS를 부유화하기 위해서 300mg ZnSO4.7H2O를 가한다.
5. Na2CO3를 가해서 pH9로 적정한다. (pH종이 이용)
6. 교반기를 낮은 속도 (약 500mm-1)로 20여분간 공기의 공급이 없이 회전시킨다.
7. 그 다음 현탁액 속에 100mg의 Potassium-ethylxanthate와 pine oil 3방울 을 떨어뜨린 후 임펠러의 속도를 2500 mm-1로 증가시킨다. 이때, 밸브는 열 지 않는다.
8. 1분간 강력하게 교반한 후 공기 밸브를 열면 회청색의 부유물이 흘러내린다. 이를 손 긁개를 이용해 자기 접시에 모은다. PbS의 부유화는 10분간 게속된 다. 이 과정을 계속하는 동안 임펠러의 속도를 3000mm-1로 증가시킨다.
9. 수집된 PbS의 부유물을 거른 후 물에 헹구어 오븐에서 건조시킨다.
10. PbS 부유물을 건조시키는 동안 ZnS의 부유화를 하기 위해 남아 있는 광물에 200mg 의 CuSO4를 가한 후 전과 동일한 다음과 같은 방법을 거친다.
11. 교반용기의 표시된 선까지 물을 채우고 pH를 조절. (Na2CO3로 조절)
12.교반기를 500mm-1속도로 10분간 회전시킨 후, 100mg의 Potassium -ethylxanthate 와 3방울의 pine oil을 넣어 준다.
13. 공기밸브를 열어 ZnS를 부유화시키기 전에 1분간 임펠러의 속도를 2500mm-1 로 증가시 킨다.
14. ZnS의 부유물을 앞에서 서술한 PbS와 같은 과정으로 수거한다.
15. 끝으로, 남아 있는 광물을 전부 거른 후 헹구어 오븐에서 건조시킨다.
16. 3개의 부유석출물 PbS, ZnS, 맥석광물의 무게를 잰다.
17. PbS, ZnS, 맥석광물의 분율밀도와 광물 자체의 밀도를 측정한다.
18. 아래와 같은 입자 크기를 가진 두 개의 다른 광석에도 정확한 조작을 되풀이 한다.
- < 0.06 mm
- 0.2와 0.4 mm 사이
ZnSO4 (Zinc Sulfate)
- mol wt : 161.44
- O : 39.64%, S : 19.86%, Zn : 40.50%
- Monohydrate, dried zinc sulfate.
- Powder or granules
- Sol in water, practically isol in alcohol
- Odorles crystals or granules or powder
- Efflorescent in dry air
- d : 1.97, m.p : 100°
- One gram dissolves in 0.6ml water
- Use : As mordant in calico-printing ; preserring wood and skins ; with hypo-chlorite for bleaching paper. manuf lithpone and other zinc salts ; clarifying glue ; electrodepositing Zn ; also as reagent in analytical chemistry.
Lime (Calcium Oxide)
- mol wt : 56.08
- Ca : 71.47%, O : 28.53%
- Properly stored lime of commerce contains 90~95% free CaO.
- Commercial production from limestone.
- Crystals, white or grayish-white humps, or granular powder.
- m.p : 2572°, b.p : 2850°, d 3.32~3.35
- Sol in water forming Ca(OH)2 and generating a large quenting of heat.
H2SO4 (Sulfuric Acid)
- mol wt : 98.08
- H : 2.06%, O : 65.25%, S : 32.69%
- Sulfuric acid of commerce contains 93~98°
- Clear, colorless, odorless, oily liquid.
- d : 1.84, b.p : 290°
Na2CO3 (Sodium Carbonate)
- mol wt : 106.00
- C : 11.33%, Na : 43.39%, O : 45.29%
- Occurs in nature as the hydrate, thermonatrite, and the decahydrate, natron or natrite.
- Odorless, hygroscopic powder.
- m.p : 851°, d : 2.53
- Use : In manuf of Na salts, glass, soap ; for washing wood ; textiles, etc ; in bleaching linen, cotton ; general cleanser ; in water - softening in photography
(3). 실험 장치
실험에서 사용된 부유화 장치는 회분식으로 작동하는 배부유화통(WEDAG)인 실험실적 부유화 용기로 그림 6에 개략적으로 나타내었다. 기계적 교반과 현탁액내의 공기공급은 위쪽 축S와 연결된 임펠러 I의 회전으로 이루어진다. 회전체는 공기 입구 A를 지나 임펠러축내 공간을 통해 들어오는 공기와 H관을 통해 들어오는 현탁액을 밑으로 끌어내린다. 완전한 교반후 기포가 섞인 현탁액은 임펠러 주위의 정체 공간으로 배출된다. 임펠러의 속도는 계속적으로 조절되며 공기의 유입은 밸브V에 의해서 조절된다. 표시 M까지 채운 용기의 부피는 2.5ℓ이다. 부유화된 광물은 손긁개에 의해서 지점 O로 흘러내리게 한다.
그림 6. 개략적으로 그린 실험실용 부유화 장치
(4). 실험 방법
본격적인 실험 절차는 다음과 같다.
1. 광석을 cross beater mill로 거의 혹은 완전히 광물이 유리될 때까지 분쇄한다.
2. 채로 쳐서 0.06~0.15mm사이의 광물 입자를 준비한다.
3. 물과 150g의 광석 분말을 혼합한 현탁액을 부유화 용기 내에 표시
된 지점(약 2.5ℓ)까 지 가득 채운다.
4. PbS를 부유화하기 위해서 300mg ZnSO4.7H2O를 가한다.
5. Na2CO3를 가해서 pH9로 적정한다. (pH종이 이용)
6. 교반기를 낮은 속도 (약 500mm-1)로 20여분간 공기의 공급이 없이 회전시킨다.
7. 그 다음 현탁액 속에 100mg의 Potassium-ethylxanthate와 pine oil 3방울 을 떨어뜨린 후 임펠러의 속도를 2500 mm-1로 증가시킨다. 이때, 밸브는 열 지 않는다.
8. 1분간 강력하게 교반한 후 공기 밸브를 열면 회청색의 부유물이 흘러내린다. 이를 손 긁개를 이용해 자기 접시에 모은다. PbS의 부유화는 10분간 게속된 다. 이 과정을 계속하는 동안 임펠러의 속도를 3000mm-1로 증가시킨다.
9. 수집된 PbS의 부유물을 거른 후 물에 헹구어 오븐에서 건조시킨다.
10. PbS 부유물을 건조시키는 동안 ZnS의 부유화를 하기 위해 남아 있는 광물에 200mg 의 CuSO4를 가한 후 전과 동일한 다음과 같은 방법을 거친다.
11. 교반용기의 표시된 선까지 물을 채우고 pH를 조절. (Na2CO3로 조절)
12.교반기를 500mm-1속도로 10분간 회전시킨 후, 100mg의 Potassium -ethylxanthate 와 3방울의 pine oil을 넣어 준다.
13. 공기밸브를 열어 ZnS를 부유화시키기 전에 1분간 임펠러의 속도를 2500mm-1 로 증가시 킨다.
14. ZnS의 부유물을 앞에서 서술한 PbS와 같은 과정으로 수거한다.
15. 끝으로, 남아 있는 광물을 전부 거른 후 헹구어 오븐에서 건조시킨다.
16. 3개의 부유석출물 PbS, ZnS, 맥석광물의 무게를 잰다.
17. PbS, ZnS, 맥석광물의 분율밀도와 광물 자체의 밀도를 측정한다.
18. 아래와 같은 입자 크기를 가진 두 개의 다른 광석에도 정확한 조작을 되풀이 한다.
- < 0.06 mm
- 0.2와 0.4 mm 사이